(12) UK Patent Application
`
`(19) G 8 (11) 2 213 793(13)A
`
`(43) Date of A publication 23.08.1989
`
`(51) INT CL•
`B65H 81/00
`
`(52) UK CL (Edition J)
`B8G G1D G4
`
`(56) Documents cited
`GB 1160021 A GB 1114657 A
`US 4170505 A
`
`EP 0265915 A2
`
`(58) Field of search
`UK CL (Edition J) BBG
`INTCL' 865H
`
`(21) Application No 8826325.6
`
`(22) Date of filing 10.11.1988
`
`(30) Priority data
`(31) 3743485
`
`(32) 22.12.1987
`
`(33) OE
`
`(71) Applicant
`MTU Motoren-und Turblnen-Union Munchen GmbH
`
`(Incorporated In the Federal Republic of Germany)
`
`Postfach 50 06 40, 8000 Munchen 50,
`Oachauer Strasse 665, Federal Republic of Germany
`
`(72) Inventor
`Dr Berhard Wohrl
`
`(74) Agent and/or Address for Service
`Withers & Rogers
`4 Dyer's Buildings, Holborn, London, EC1 N 2JT,
`United Kingdom
`
`(54) Winding airfoil
`
`In the manufacture of a three-dimensionally twisted airfoil of a rotor blade, a fibre strand 9 is continuously impregnated
`(57)
`with resin material, pressed by roller 11 on to an airfoil surface 1 and immediately precured at 15. The method permits the
`fast, simple and fully automatic manufacture of airfoils. The precuring device 15 may be an infrared radiator. The strand
`may be looped around nipples on a blade root. The winding device may be a six-axis robot. The precured airfoil is cured in
`a mould.
`
`10
`
`At least one drawing originally filed was informal and the print reproduced here is taken from a later filed formal copy.
`
`FIG. 2
`
`G)
`OJ
`(\.)
`['\.)
`__.._
`w
`-.J
`(0
`w
`)>
`
`Page 1 of 9
`
`Markforged Ex. 1010
`Markforged v. Continuous Composites, IPR2022-01220
`
`

`

`1 /2
`
`FIG. 1
`
`15
`
`11
`
`8
`
`FIG.3
`
`Page 2 of 9
`
`Markforged Ex. 1010
`Markforged v. Continuous Composites, IPR2022-01220
`
`

`

`2/2
`
`2213'793
`
`16
`
`10
`
`FIG. 2
`
`;.
`
`Page 3 of 9
`
`Markforged Ex. 1010
`Markforged v. Continuous Composites, IPR2022-01220
`
`

`

`-1-
`
`2213193
`
`METHOD FOR MANUFACTURING A THREE-DIMENSIONALLY
`TWISTED ROTOR BLADE AIRFOIL
`
`This invention relates to a method for the manufacture
`
`of a fibre reinforced component, particularly a three(cid:173)
`
`dimensionally twisted rotor blade airfoil, by wrapping
`
`a core with a resin-impregnated fibre material,
`
`5
`
`Fibre components are rapidly gaining technical
`
`significance on account of their excellent properties.
`
`Their low density, high tensile strength and relative
`
`ease of shaping invites their use in areas that had
`
`formerly been the sole domain of metallic materials.
`
`10 Fibre-reinforced materials, e,g. are also finding use
`
`in aircraft applications, as for dynamically highly stressed
`
`rotor blades and propellers or for propfan airfoils.
`
`Another outstanding property of fibre-reinforced
`
`materials is the option of influencing component properties
`
`15 by laying the fibres in preferred orientation to obtain
`
`different material data in different directions for, e.g.
`
`the modulus of elasticity or damping constants.
`
`Technical problems are encountered, however, in the
`
`manufacture of fibre-reinforced components of complex
`
`20 shapes with three-dimensionally twisted surfaces, especially
`
`if these take a partially concave form and if the
`
`requirements are for different strength and vibration
`
`properties in different directions, This applies
`
`particularly to modern turbine engine fan or propan blades,
`
`25 where the attachment of the airfoil to the root or rotor
`
`poses another specific problem.
`
`Page 4 of 9
`
`Markforged Ex. 1010
`Markforged v. Continuous Composites, IPR2022-01220
`
`

`

`Conventional manufacture of these components is associated
`
`-2-
`
`with considerable effort involving high manufacturing
`
`costs.
`
`It employs so-called prepegs, which are fibre
`
`panels impregnated with a matrix material and inserted in
`
`5
`
`a hollow mould to be cured under pressure and heat. One
`
`disadvantage of this method is the extremely high cost
`
`involved when trying to deliberately influence component
`
`properties with it, which basically is a feasible
`
`proposition.
`
`10
`
`One object of this invention is to enable the manufacture
`
`of a fibre-reinforced component, particularly a three(cid:173)
`
`dimensionally twisted rotor blade airfoil by a simple and
`
`rapid method that permits selective manipulation of
`
`component properties by selective routing of the fibres
`
`15
`
`and more particularly so as to permit ready application of
`
`fibres also to concave surfaces.
`
`According to this invention we propose a method for the
`
`manufacture of a fibre-reinforced component such as
`
`an airfoil, particularly a three-dimensionally t~isted
`
`20
`
`rotor blade airfoil by wrapping a core with a resin
`
`impregnated fibre material, wherein fibre strands wetted
`
`with a resin matrix are pressed against the core for
`
`example, by means of a nip roller, and the resin matrix
`
`precured immediately thereafter, preferably by a precuring
`
`25
`
`facility such as an infrared radiator coupled to the nip
`
`roller.
`
`Fibres can be applied in a simple manner, in each and
`
`every direction and on any shape of airfoil surface and
`
`Page 5 of 9
`
`Markforged Ex. 1010
`Markforged v. Continuous Composites, IPR2022-01220
`
`

`

`' '
`
`-3-
`
`so that they will then adhere and not subsequently become
`
`dislodged. After the fibres have precured they will
`
`adhere also to concave surfaces,. so they can be laid
`
`rapidly and accurately in position. Depending on
`
`5
`
`requirements several plies of fibre can be deposited one
`
`over the other in different or identical orientations.
`
`Precuring the matrix material causes it to gel to a
`
`point where the fibre is cemented in place before the
`
`fibre matrix mixture still is fully cured. Thereafter
`
`10
`
`the wrapped component is pressed to final size in a mould
`
`and cured in a furnace.
`
`The time needed to manufacture a twisted fibre
`
`component is substantially shorter than that expended in
`
`conventional manufacture, An essential consideration
`
`15 also is that concave blades can simply and accurately
`
`be covered with layers of fibre, which with the
`
`conventional methods of fibre application cannct be
`
`achieved with full satisfaction.
`
`This much simplifies the wrapping process and so makes
`
`20
`
`it susceptible of fully automated computer and robot
`
`controlled implementation,
`
`The fibre strands can advantageously be laid along
`
`preferred tracks. This permits a selective anisotropic
`
`component structure to be achieved in arrangements
`
`25 benefiting stability and strength.
`
`This helps eliminate
`
`especially vibration problems.
`
`In a preferred embodiment, the fibre strands are looped
`
`around a number of attaching nipples on the blade root to
`
`Page 6 of 9
`
`Markforged Ex. 1010
`Markforged v. Continuous Composites, IPR2022-01220
`
`

`

`-4-
`
`attach the airfoil to the root. This permits a
`
`particularly favourable transfer of the centrifugal forces
`
`acting on the root in operation.
`
`Embodiments of the present invention will now be
`
`5
`
`described by way of example with reference to the
`
`accompanying drawings, in which
`
`Figure 1 is a perspective view illustrating a fan blade;
`
`Figure 2 is a perspective view illustrating a fibre
`
`laying device; and
`
`10
`
`Figure 3 is a perspective view illustrating a six-axis
`
`portal robot.
`
`With reference now to Figure 1
`
`the airfoil 1 of
`
`a rotor blade is shown. Depicted also are the preferred
`
`directions of the fibres to be deposited: the main
`
`15
`
`tensile direction 2 and the diagonal layers 3 and 4.
`
`The
`
`fibres are preferably looped around attaching nipples
`
`5 on a blade root 6, so as to ensure a satisfactory union
`
`between the two components and for good transfer to the
`
`blade root 6 of the tensile force arising in operation.
`
`20
`
`The fibre laying device 8 shown in Figure 2
`
`essentially comprises a fibre drum 10, a fibre feed duct
`
`12 leading to a fibre nip roll 11, and a precuring
`
`facility 15. The fibre strand 9 unwound from the fibre
`
`drum 10 is pulled by the nip roll 11 through the fibre
`
`25
`
`feed duct 12 into which matrix material is fed in defined
`
`"'.Ii
`
`quantities from a matrix metering unit 14 through a feed
`
`duct 13. The matrix material is supplied from a storage
`
`container 16 to the matrix metering unit 14 through a
`
`Page 7 of 9
`
`Markforged Ex. 1010
`Markforged v. Continuous Composites, IPR2022-01220
`
`

`

`-5-
`
`flexible feed line 17. The volume of matrix fed per unit
`
`length of fibre can be adjusted, preferably to suit the
`
`fibre throughput. Having been wetted in this manner the
`
`fibres are accurately laid on to the component in the
`
`5 desired track under the fibre nip roll 11 and are precured
`
`(gelled) by means of the precuring device 15, causing the
`
`surface to dry and stick,
`
`In this manner, the
`
`:ibre is
`
`fixed to a point where it can be laid on to radiused tracks.
`
`Thereafter, further fibre layers can be deposited in any
`
`lOdesired orientation over the precured fibres.
`
`As it will become apparent from Figure 3, the fibre
`
`laying device 8 here shown in schematic arrangement is
`
`connected to the "wrist" of a six-axis portal robot 7
`
`and can thus - under computer control - deposit the fibre
`
`15strand
`
`9 on the component core fully automatically along
`
`precalculated tracks. This makes for very accurate
`
`reproducibility ( <0.2 mm) cf the fibre laying process.
`
`The rough item having been manufactured in this manner,
`
`is then placed in a mould and conventionally finish
`
`20cured under pressure and heat.
`
`Page 8 of 9
`
`Markforged Ex. 1010
`Markforged v. Continuous Composites, IPR2022-01220
`
`

`

`-6-
`
`CLAIMS
`
`1.
`
`A method for the manufacture of a fibre-reinfcrcedx
`
`component by wrapping a core with a resin-impregnated
`
`fibre material, wherein fibre strands wetted wi~n a resin
`
`matrix are pressed against the core and the resin natrix
`
`5
`
`precured immediately thereafter.
`
`2.
`
`A method according to claim 1 wherein the wetted
`
`fibre strands are pressed against the core by a nip roller
`
`having coupled thereto a resin matrix precuring facility.
`
`3.
`
`A method according to claim 1 wherein the co~ponent
`
`10 is an airfoil and the fibre strands are looped around a
`
`number of attaching nipples on a blade root to sec~re the
`
`airfoil to the blade root (6).
`
`4.
`
`A method according to claim 2, wherein the precuring
`
`facility comprises an infrared radiator.
`
`15 5.
`
`A method according to claim
`
`2 wherein the f~bre
`
`strands are drawn through a fibre fe~d d~2t
`
`matrix material is introduced to wet fibre strands.
`
`6.
`
`A method for the manufacture of fibre reinforced
`
`component, particularly a three-dimensionally twisted
`
`20 airfoil, substantially as hereinbefore described with
`
`reference to the accompanying drawings.
`
`PubhsheC 1988 at The Patent Offlce. Sts.:.; House. 66 "71 H1g:i-~ Ro:borr... Londc:--. WClR 4T? F-..:r..he:- cop!es may be oC:air..1;;.:! fro;:;:-. T"ne Pa.tent Off1C'::"
`Sales Brancl:., St !.fa.=:;· Cray. Orp:mg:or... Ken:. BR5 3RD Prmted by M:ttltlplex tecf'..r-...1ques lt.c. St Ma~- Cra:•- Ker..t Car ... l 87
`
`Page 9 of 9
`
`Markforged Ex. 1010
`Markforged v. Continuous Composites, IPR2022-01220
`
`

This document is available on Docket Alarm but you must sign up to view it.


Or .

Accessing this document will incur an additional charge of $.

After purchase, you can access this document again without charge.

Accept $ Charge
throbber

Still Working On It

This document is taking longer than usual to download. This can happen if we need to contact the court directly to obtain the document and their servers are running slowly.

Give it another minute or two to complete, and then try the refresh button.

throbber

A few More Minutes ... Still Working

It can take up to 5 minutes for us to download a document if the court servers are running slowly.

Thank you for your continued patience.

This document could not be displayed.

We could not find this document within its docket. Please go back to the docket page and check the link. If that does not work, go back to the docket and refresh it to pull the newest information.

Your account does not support viewing this document.

You need a Paid Account to view this document. Click here to change your account type.

Your account does not support viewing this document.

Set your membership status to view this document.

With a Docket Alarm membership, you'll get a whole lot more, including:

  • Up-to-date information for this case.
  • Email alerts whenever there is an update.
  • Full text search for other cases.
  • Get email alerts whenever a new case matches your search.

Become a Member

One Moment Please

The filing “” is large (MB) and is being downloaded.

Please refresh this page in a few minutes to see if the filing has been downloaded. The filing will also be emailed to you when the download completes.

Your document is on its way!

If you do not receive the document in five minutes, contact support at support@docketalarm.com.

Sealed Document

We are unable to display this document, it may be under a court ordered seal.

If you have proper credentials to access the file, you may proceed directly to the court's system using your government issued username and password.


Access Government Site

We are redirecting you
to a mobile optimized page.





Document Unreadable or Corrupt

Refresh this Document
Go to the Docket

We are unable to display this document.

Refresh this Document
Go to the Docket